| 牌号 | Cu% | Sn % | Zn % |
| FDCuSn10 | 88~91 | 其餘 | |
| FDCuSn 15 | 78~81 | 其餘 | |
| FDCuSn 20 βφ• | 68.5~71.5 | 其餘 | 0 |
| FDCuSn6Zn6 | 餘量 | 5~7 | 5~7 |
| 牌号 | 規格 | 粒徑組成(質量分(fēn)數(shù))/% |
松裝密度 g/cm³ |
流動性 s/50g |
|||
| ≥150μm | 150μm~75μm | 75μm～45μm | ≤45μm | ||||
| FDCuSn&×≤10 | 150μm | ≤3 | 20~30 | 30~40 | ≤55 | 2.0~2.6 | ≤45 |
| 75μm | ≤3 | 15~35 | ≥65 | 2.0~2.8 | ≤45 | ||
| 45μm | — | ≤3 | ≥97 | 2.4~2.6 | |||
| FDCuSn15 | 150μm | ≤3 | 20~30 | 30~40 | ≤55 | 2.0~2.6 | ≤45 |
| 75μm | ≤3 | 15~35 | ≥65 | 2.0~2.8 | ≤45 | ||
| 45μm | ≤3 | ≥97 | 2.4~2.6 | ||||
| FDCuSn20 | 150μm | ≤3 | 20~30 | 30~40 | ≤55 | 2.0~2.6 | ≤45 |
| 74μm | ≤3 | 15~35 | ≥65 | 2.0~2.8 | ≤45 | ||
| 45μm | ≤3 | ≥97 | 2.4~2.6 | ||||
| FDCuSn6Zn6 ₹£÷ | 150μm | ≤3 | 20~30 | 30~40 | ≤55 | 2.0~2.6 | ≤45 |
| 74μm | ≤3 | 15~35 | ≥65 | 2.0~2.8 | ≤45 | ||
| 45μm | ≤3 | ≥97 | 2.4~2.6 | ||||
| 化(huà)學成分(fēn)(質量分(fēn)數(≤↑€shù))/% | ||||||||
|
Cu+Sn+Zn
不(bù) &∏∑₹nbsp; 于
|
雜(zá)質(不(bù)大(dà)于& ₽ ) | |||||||
| 99.5 | Fe | Pb | As | Cd | Hg | Cr | 0 | 總和(hé) |
| 0.05 | 0.05 | 0.005 | 0.005 | 0.005 | 0.005 | 0.1 | 0.5 | |
|
注1:如(rú)需方對(duì)φ₽産品化(huà)學成分(fēn)有(yǒu)特殊要(yào)求，由供需雙方協γ∑商。 注2:化(huà)學成分(fēn)中不(bù)包括添←∑★✘加劑，如(rú)加添加劑，标明(míng)所£≤加添加劑名稱和(hé)添加量。 |
||||||||
| 産品牌号 | 燒結收縮率 96 | 松裝密度 g/cm |
流動性 s/50s |
壓縮性 g/cm° |
生(shēng)坯強度 (MPa) |
徑向壓潰強度 (MPa) |
| FDCuSn10 | 1.2~1.4 | 2.2~3.0 | <45 | >7.2 | >8 | >180 |
| FDCuSn15 | 1.4~1.6 | 2.2~3.0 | <45 | >7.2 | >8 | >160 |
| FDCuSn20 | 1.4~1.6 | 2.2~3.0 | <45 | >7.2 | >8 | >160 |
| FDCuSn6Zn6 | 1.2~1.4 | 2.2~3.0 | <45 | >7.2 | >8 | >180 |
| 備注：測試收縮率的(de)條件(♠∞jiàn)，壓制(zhì)密度6.2g/c•δm³,350攝氏度下(xià)預氧化(huà)脫蠟30min,在7±λ♥©00℃下(xià)燒結30min | ||||||